Tambaga interolloy piring aloi 25 C17200 tambaga
Komposisi kimia
| Elemen | Komponén |
| Be | 1.85-2.10% |
| Co + ni | 0,20% mnt |
| CO + Ni + FE | 0,60% maksimal. |
| Cu | Kasaimbangan |
Pasipatan fisik khas
| Kapadetan (g / cm3) | 8.36 |
| Kapadetan sateuacan umur hardening (g / cm3 | 8.25 |
| Modulus Elice (kg / mm2 (103))) | 13.40 |
| Koefision termal termal (20 ° C ka 200 ° C m / m / ° c) | 17 x 10-6 |
| Kanyataanitas termal (cal / (cm-(cm-s- ° c)) | 0,25 |
| Jarak lebur (° C) | 870-980 |
Harta mékanis (sateuacan perlakuan hardening):
| status | Kakuatan regangan (Kg / mm3) | Gangguan susuk (Hv) | Kondangaan (Iacs%) | Elongasi (%) |
| H | 70-85 | 210-240 | 22 | 2-8 |
| 1 / 2h | 60-71 | 160-210 | 22 | 5-25 |
| 0 | 42-55 | 90-160 | 22 | 35-70 |
Saatos perawatan
| Merek | Kakuatan regangan (Kg / mm3) | Gangguan susuk (Hv) | Kondangaan (Iacs%) | Elongasi (%) |
| C17200-Tm06 | 1070-1210 | 330-390 | ≥17 | ≥4 |
Fitur
1. Kanyataanitas termal tinggi
2. Rintésan korosi tinggi, khususna cocog pikeun polyoksidilén (PVC) kapang teuing.
3. Karepasan tinggi, ngagem résistansi sareng
4. Perajian Polamming katingali, tiasa ngahontal éngkon sanésna, desain real luhur sareng desain rumit.
5. Résistinsi ticting anu saé, gampang digarming sareng logam sanés, gampang mesin, moal aya perlakuan panas tambahan.